| 性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | ||
| 物理性能 | 填充含量 | 30 | Wt% | |||
| 比重 | ASTM D792 | 1.52 | ||||
| 吸水率 | 23℃,24hr | ASTM D570 | 0.07 | % | ||
| 成型收縮率 | - | 平行方向 | 0.2 | % | ||
| - | 垂直方向 | 0.7 | % | |||
| 機械性能 | 拉伸強度 | ASTM D638 | 132.4 | MPa | ||
| 拉伸長度 | ASTM D638 | 4 | % | |||
| 彎曲強度 | ASTM D790 | 196.1 | MPa | |||
| 彎曲模量 | ASTM D790 | 7.85 | Gpa | |||
| Izod缺口沖擊強度 | 3.2mm | ASTM D256 | 98 | J/M | ||
| 洛氏硬度 | ASTM D785 | 120 | R | |||
| 摩擦系數(shù) | ASTM D1894 | 0.15 | ||||
| 電氣性能 | 介電常數(shù) | 106Hz | ASTM D150 | 30 | pF/m | |
| 介電損耗正切值 | 106Hz | ASTM D150 | 0.016 | |||
| 體積電阻系數(shù) | ASTM D257 | 1016 | ||||
| 耐電壓 | ASTM D149 | 25 | KV/mm | |||
| 電弧電阻系數(shù) | ASTM D495 | 130 | S | |||
| 熱性能 | 熔點 | DSC法 | 224 | ℃ | ||
| 負荷撓曲溫度 | - | 0.45MPa | ASTM D648 | 220 | ℃ | |
| - | 1.86Mpa | ASTM D648 | 215 | ℃ | ||
| 線膨脹系數(shù) | 3.0 | |||||
| 阻燃性 | UL94 | HB | ||||
| 比熱 | 0.5 | |||||