| 性能項(xiàng)目 | 試驗(yàn)條件[狀態(tài)] | 測(cè)試方法 | 測(cè)試數(shù)據(jù) | 數(shù)據(jù)單位 | ||
| 基本性能 | 24小時(shí)吸水率 | ASTM D-570 | 0.3 | % | ||
| 物理性能 | 泰伯磨耗量 | H 18輪 | ASTM D-1044 | 47 | mg/1000rev | |
| 比重 | ASTM D-792 | 1.25 | ||||
| 泰伯磨耗量 | CS-17輪 | ASTM D-1044 | 13 | mg/1000rev | ||
| 熔體流動(dòng)速率 | ASTM D-1238 | 12.5 | g/10min | |||
| 機(jī)械性能 | 硬度計(jì)硬度 | ASTM D-2240 | 72 | |||
| 斷裂伸長(zhǎng) | ASTM D-638 | 360 | % | |||
| 拉伸力 | 5%伸長(zhǎng) | ASTM D-638 | 14 | MPa | ||
| 10%伸長(zhǎng) | ASTM D-638 | 20 | MPa | |||
| 斷裂拉伸力 | ASTM D-638 | 45.8 | MPa | |||
| 埃佐沖擊強(qiáng)度 | 23℃ | ASTM D-256 | 210 | J/m | ||
| 揉曲模量 | 23℃ | ASTM D-790 | 570 | MPa | ||
| 初耐撕裂性能 | ASTM D-1004 | 200 | kn/m | |||
| 熱性能 | 熱畸變溫度 | @0.5MPa | ASTM D-648 | 130 | ℃ | |
| 維卡軟化點(diǎn) | ASTM D-1525 | 207 | ℃ | |||
| 熔點(diǎn) | ASTM D-3418 | 218 | ℃ | |||
| 熱畸變溫度 | @0.18MPa | ASTM D-648 | 52 | ℃ | ||
| 其它性能 | 耐揉曲切口增長(zhǎng)性能 | ASTM D-1052 | >3×104 | |||
美國(guó)杜邦 Hytrel? 7246
THERMOPLASTIC POLYESTER ELASTOMER
美國(guó)杜邦 TPE 7246產(chǎn)品說(shuō)明:
72 Shore D High Performance Polyester Elastomer
添加劑 |
|
RoHS 合規(guī)性 |
|
形式 |
|
加工方法 | 薄膜擠出擠出澆鑄片材擠出成型熱成型涂層型材擠出成型注射成型 |
| TPE 7246物理性能 | 額定值 | 單位制 | 測(cè)試方法 |
密度 | 1.26 | g/cm3 | ISO 1183 |
熔流率（熔體流動(dòng)速率） (240°C/2.16 kg) | 13 | g/10 min | ISO 1133 |
溶化體積流率（MVR） (240°C/2.16 kg) | 0.732 | in3/10min | ISO 1133 |
收縮率 | ISO 294-4 | ||
橫向流量 | 1.6 | % | |
流量 | 1.6 | % | |
吸水率 | ISO 62 | ||
73°F, 24 hr | 0.30 | % | |
飽和, 73°F, 0.0787 in | 0.60 | % | |
平衡, 73°F, 0.0787 in, 50% RH | 0.20 | % | |
| 硬度 | 額定值 | 單位制 | 測(cè)試方法 |
肖氏硬度 | ISO 868 | ||
邵氏 D | 68 | ||
邵氏 D, 15 秒 | 64 |
要了解更多關(guān)于美國(guó)杜邦 TPE 7246的相關(guān)資料報(bào)告，請(qǐng)聯(lián)系我們