產(chǎn)品參數(shù)
| 性能項(xiàng)目 | 測(cè)試方法 | 測(cè)試條件 | 測(cè)試數(shù)據(jù) | 數(shù)據(jù)單位 | |
| 物理性能 | 比重 | ASTM D792 | 1.17 | g/cm3 | |
| 表觀密度 | ASTM D1895 | 0.71 | g/cm3 | ||
| 熔體流動(dòng)速率 | ASTM D1238 | 230℃，3.8kg | 13 | g/10min | |
| 成型收縮率 | ASTM D955 | 流動(dòng) | 0.3-0.6 | % | |
| 吸水率 | ASTM D570 | 飽和 | 0.30 | % | |
| 機(jī)械性能 | 洛氏硬度 | ASTM D785 | 65 | ||
| 拉伸模量 | ASTM D638 | 2280 | MPa | ||
| 拉伸強(qiáng)度 | ASTM D638 | 56.5 | MPa | ||
| 拉伸伸長率 | ASTM D638 | 屈服 | 5.0 | % | |
| 拉伸伸長率 | ASTM D638 | 斷裂 | 25 | % | |
| 彎曲模量 | ASTM D790 | 2000 | MPa | ||
| 彎曲強(qiáng)度 | ASTM D790 | 68.9 | MPa | ||
| 懸臂梁缺口沖擊強(qiáng)度 | ASTM D256 | 0℃，6.35mm | 24 | J/m | |
| 懸臂梁缺口沖擊強(qiáng)度 | ASTM D256 | 23℃，6.35mm | 40 | J/m | |
| 熱性能 | 熱變形溫度 | ASTM D648 | 1.8MPa，退火 | 91.1 | ℃ |
| 維卡軟化溫度 | ASTM D1525 | 97.8 | ℃ | ||
| 線形膨脹系數(shù) | ASTM D696 | 流動(dòng)，0-100℃ | 0.000072 | cm/cm/℃ | |
| 光學(xué)性能 | 透射率 | ASTM D1003 | 3200微米 | 92 | % |
| 渾濁 | ASTM D1003 | 3200微米 | 1.0 | % | |
| 黃度指數(shù) | ASTM D1925 | 3.20mm | 0.30 | YI | |