產(chǎn)品參數(shù)
| 性能項(xiàng)目 | 試驗(yàn)條件[狀態(tài)] | 測(cè)試方法 | 測(cè)試數(shù)據(jù) | 數(shù)據(jù)單位 | |
| 基本性能 | 吸水率 | 23.C 60%RH | ASTM D-570 | 0.22 | % |
| 熔體流動(dòng)速率 | ASTM D-1237 | 9 | G/10min | ||
| 物理性能 | 比重 | ASTM D-792 | 1.41 | ||
| 機(jī)械性能 | 拉伸強(qiáng)度 | 1.6mm | ASTM D-1822 | 98 | KJ/m2 |
| 拉伸長度 | 23℃ | ASTM D-638 | 50 | % | |
| 拉伸強(qiáng)度 | 23℃ | ASTM D-638 | 62.3 | MPa | |
| 撓曲強(qiáng)度 | 23℃ | ASTM D-790 | 91.2 | MPa | |
| 洛氏硬度 | ASTM D-785 | 80 | M scale | ||
| IZOD沖擊強(qiáng)度 | 3.2mm | ASTM D-256 | 54 | J/m | |
| 彎曲模量 | 23℃ | ASTM D-790 | 2.62 | GPa | |
| 撕裂強(qiáng)度 | 2mm | ASTM D-732 | 54.9 | MPa | |
| 電氣性能 | 體積電阻系數(shù) | ASTM D-257 | 1×1014/ | ||
| 介電常數(shù) | 106Hz | ASTM D-150 | 33 | Pf/m | |
| 表面電阻系數(shù) | ASTM D-257 | 1×1016 | |||
| 介電損耗正切 | 106Hz | ASTM D-150 | 0.007 | ||
| 耐電壓 | ASTM D-149 | 19 | MV/m | ||
| 加工性能 | 成型收縮率 | 平行方向 | 20 | % | |
| 熱性能 | 燃燒性 | UL 94 | HB | ||
| 熔點(diǎn) | 10℃/min | DSC | 165 | ℃ | |
| 負(fù)荷撓曲溫度 | 455kPa | ASTM D-648 | 158 | ℃ | |
| 負(fù)荷撓曲溫度 | 820kPa | ASTM D-648 | 110 | ℃ | |
| 線膨脹系數(shù) | 20℃-80℃ | ASTM D-696 | 13 | 10 | |
POM塑料
（聚甲醛）（賽鋼~特靈）
英文名稱：Polyoxymethylene(Polyformaldehyde)
POM（聚甲醛樹脂）定義：聚甲醛是一種沒有側(cè)鏈、高密度、高結(jié)晶性的線型聚合物。按其分子鏈中化學(xué)結(jié)構(gòu)的不同，可分為均聚甲醛和共聚甲醛兩種。兩者的重要區(qū)別是：均聚甲醛密度、結(jié)晶度、熔點(diǎn)都高，但熱穩(wěn)定性差，加工溫度范圍窄（約10℃），對(duì)酸堿穩(wěn)定性略低；而共聚甲醛密度、結(jié)晶度、熔點(diǎn)、強(qiáng)度都較低，但熱穩(wěn)定性好，不易分解，加工溫度范圍寬（約50℃），對(duì)酸堿穩(wěn)定性較好。是具有優(yōu)異的綜合性能的工程塑料。有良好的物理、機(jī)械和化學(xué)性能，尤其是有優(yōu)異的耐摩擦性能。俗稱賽鋼或奪鋼，為第三大通用工程塑料。 適于制作減磨耐磨零件，傳動(dòng)零件，以及化工，儀表等零件。
合成樹脂中的一種，又名聚甲醛樹脂、POM塑料、賽鋼料等；是一種白色或黑色塑料顆粒，具有高硬度、高鋼性、高耐磨的特性。主要用于齒輪，軸承，汽車零部件、機(jī)床、儀表內(nèi)件等起骨架作用的產(chǎn)品。