| 性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | |
| 基本性能 | 吸濕率 | 濕 | 1.7 | % | |
| 物理性能 | 比重 | 干 | ASTM D-792 | 1.39 | |
| 成型收縮率 | 干 | 旭化成方法 | 0.4/0.9 | % | |
| 磨耗率 | 濕 | ASTM D-1044 | 15 | ×10-6kg/1000times | |
| 機械性能 | 洛氏硬度 | 干(濕) | ASTM D-785 | 96(75) | M scale |
| 抗撓強度 | 干(濕) | ASTM D-790 | 289(216) | MPa | |
| 拉伸強度 | 干(濕) | ASTM D-638 | 186(132) | MPa | |
| 斷裂延伸率 | 干(濕) | ASTM D-638 | 3(5) | % | |
| 洛氏硬度 | 干(濕) | ASTM D-785 | 120(112) | R scale | |
| 懸臂梁式缺口沖擊強度 | 干(濕) | ASTM D-256 | 127(147) | J/M | |
| 抗撓系數(shù) | 干(濕) | ASTM D-790 | 9.3(6.3) | GPa | |
| 熱性能 | 熱變形溫度 | 0.46MPa,干 | ASTM D-648 | 260 | ℃ |
| 比熱容 | 干 | 1590 | J/(kg.k) | ||
| 導(dǎo)熱率 | 干 | 0.3 | W/(m.k) | ||
| 熱變形溫度 | 1.82MPa,干 | ASTM D-648 | 250 | ℃ | |
| 阻燃性 | 干 | UL 94 | HB | ||
| 線性膨脹系數(shù) | 干 | ASTM D-696 | 3 | ×10-5/K | |
| 其它性能 | 氧指數(shù) | 干 | ASTM D-2863 | 23 | % |