| 廠家(產(chǎn)地) | 日本宇部 |
|---|---|
| 牌號 | 1013NH |
| 加工級別 | 注塑級 |
| 特性級別 | 耐高溫 |
| 銷售方式 | 品牌經(jīng)銷 |
| 類型 | 標準料 |
產(chǎn)品參數(shù)
| 性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | |
| 基本性能 | 成型收縮率 | UBEmethod | 1.3 | % | |
| 吸水率 | ASTM D-570 | 1.8 | % | ||
| 吸水率 | ASTM D-570 | 10.7 | % | ||
| 成型收縮率 | UBEmethod | 1.2 | % | ||
| 物理性能 | 比重 | ASTM D-792 | 1.14 | ||
| 機械性能 | 屈服下的伸張強度 | 80° | ASTM D-638 | 200 | kgf/cm2 |
| 彎曲強度 | 80° | ASTM D-790 | 500 | kgf/cm2 | |
| 彎曲彈性率 | 80° | ASTM D-790 | 7500 | kgf/cm2 | |
| 硬度（洛氏、布氏） | 23° | ASTM D-785 | 85 | ||
| 彎曲強度 | 23° | ASTM D-790 | 400 | kgf/cm2 | |
| 彎曲彈性率 | -30° | ASTM D-790 | 30000 | kgf/cm2 | |
| 抗沖擊強度 | 23° | ASTM D-256 | 50 | kgf.cm/cm | |
| 斷裂下的伸張強度 | 23° | ASTM D-638 | 650 | kgf/cm2 | |
| TABER磨耗率 | ASTM D-1044 | 7 | mg | ||
| 硬度（洛氏、布氏） | 23° | ASTM D-785 | 55 | ||
| 抗沖擊強度 | 23° | ASTM D-256 | 6.5 | kgf.cm/cm | |
| 彎曲強度 | 80° | ASTM D-790 | 260 | kgf/cm2 | |
| 1%變形下的壓縮強度 | 23° | ASTM D-695 | 100 | kgf/cm2 | |
| 屈服下的伸張強度 | -30° | ASTM D-638 | 900 | kgf/cm2 | |
| 1%變形下的壓縮強度 | 23° | ASTM D-695 | 200 | kgf/cm2 | |
| 硬度（洛氏、布氏） | 23° | ASTM D-785 | 120 | ||
| 屈服下的延伸率 | 23° | ASTM D-638 | 8 | % | |
| 彎曲彈性率 | 80° | ASTM D-790 | 4000 | kgf/cm2 | |
| 擠剪強度 | 23° | ASTM D-732 | 650 | kgf/cm2 | |
| 屈服下的伸張強度 | 80° | ASTM D-638 | 320 | kgf/cm2 | |
| 抗沖擊強度 | -30° | ASTM D-256 | 4.5 | kgf.cm/cm | |
| 斷裂下的延伸率 | 23° | ASTM D-638 | 100 | % | |
| 屈服下的伸張強度 | 23° | ASTM D-638 | 420 | kgf/cm2 | |
| 彎曲強度 | -30° | ASTM D-790 | 1400 | kgf/cm2 | |
| 彎曲強度 | 23° | ASTM D-790 | 1100 | kgf/cm2 | |
| 斷裂下的延伸率 | 23° | ASTM D-638 | >200 | % | |
| 屈服下的伸張強度 | 23° | ASTM D-638 | 800 | kgf/cm2 | |
| 屈服下的伸張強度 | -30° | ASTM D-638 | 1100 | kgf/cm2 | |
| 擠剪強度 | 23° | ASTM D-732 | 600 | kgf/cm2 | |
| 彎曲彈性率 | 23° | ASTM D-790 | 28500 | kgf/cm2 | |
| 彎曲彈性率 | -30° | ASTM D-790 | 29000 | kgf/cm2 | |
| 彎曲彈性率 | 23° | ASTM D-790 | 7700 | kgf/cm2 | |
| 彎曲強度 | -30° | ASTM D-790 | 1300 | kgf/cm2 | |
| 電氣性能 | 體積電阻率 | ASTM D-257 | 1015 | Ω.cm | |
| 介電常數(shù) | 60HZ | ASTM D-150 | 3.9 | ||
| 介電常數(shù) | 106HZ | ASTM D-150 | 3.5 | ||
| IEC電路 | UL746 | 600+ | V | ||
| 介電損耗 | 103HZ | ASTM D-150 | 0.10 | ||
| 介電損耗 | 60HZ | ASTM D-150 | 0.10 | ||
| 絕緣耐力 | ASTM D-149 | 20 | KV/mm | ||
| 介電常數(shù) | 106HZ | ASTM D-150 | 4.5 | ||
| 介電損耗 | 106HZ | ASTM D-150 | 0.12 | ||
| 抗電弧強度 | ASTM D-495 | 122 | S | ||
| 介電損耗 | 106HZ | ASTM D-150 | 0.02 | ||
| 體積電阻率 | ASTM D-257 | 1012 | Ω.cm | ||
| 介電損耗 | 60HZ | ASTM D-150 | 0.01 | ||
| 介電常數(shù) | 60HZ | ASTM D-150 | 9.0 | ||
| 介電常數(shù) | 103HZ | ASTM D-150 | 8.0 | ||
| 介電損耗 | 103HZ | ASTM D-150 | 0.02 | ||
| 介電常數(shù) | 103HZ | ASTM D-150 | 3.8 | ||
| 熱性能 | 熱變形溫度 | 4.6kgf/cm2 | ASTM D-648 | 180 | °C |
| 燃燒率 | UL94 | V-2 | |||
| 熔點 | DSC | 215-225 | °C | ||
| 熱變形溫度 | 18.6kgf/cm2 | ASTM D-648 | 75 | °C | |
| 線性熱膨脹系數(shù) | ASTM D-696 | 8 | X的10-5cm/cm/°C | ||